Changes in hardness and resilience of i‐gelTM cuffs with temperature: a benchtop study
MetadataDangos cofnod eitem llawn
The i‐gelTM is a supraglottic airway with a gel‐like thermoplastic cuff. It has been suggested that the seal around the larynx improves following insertion. Perhaps the most intuitive hypothesis proposed for this is that cuff softening occurs during warming from ambient to body temperature. We investigated this using a food industry texture analyser over a wide temperature range. Size 2 and 3 i‐gels were secured to a platform within a temperature‐controlled water bath, which was in turn mounted on a texture analyser test stand. Both water and i‐gel cuff temperatures were recorded. A spherical probe was advanced 4 mm into the surface of each i‐gel at a rate of 1 mm.s−1, then retracted at the same rate while the upward pressure on the probe was recorded. Three runs made at each of the 11 temperatures (10 °C to 60 °C, 5 °C increments) gave 105,864 data points, from which values for hardness (the peak force on the probe at maximum indentation), and resilience (the rate at which the material recovers its original shape) were calculated. Over 10 to 60 °C, the smallest hardness value expressed as a proportion of the largest was 88.2% and 89.8% for size 2 and 3 i‐gels, respectively, and for resilience these were 92.8% and 86.2%, respectively. Over room temperature to body temperature range (21–37.4 °C), hardness decreased by 3.15% and increased by 0.47% for i‐gel sizes 2 and 3, respectively, whereas resilience values decreased by 1.85% and 2.68%, respectively. Cuff hardness and resilience did generally reduce with warming, but the effect was minimal over temperature ranges that may be encountered during clinical use.
Dingley, J., Stephenson, J., Allender, V., Dawson, S. and Williams, D. (2018) 'Changes in hardness and resilience of i‐gel TM cuffs with temperature: a benchtop study', Anaesthesia, 73(7), pp.856-862. DOI: 10.1111/anae.14300.
Dynodwr Gwrthrych Digidol (DOI)https://doi.org/10.1111/anae.14300
Article published in Anaesthesia on 03 May 2018, available at: https://doi.org/10.1111/anae.14300.
Cardiff Metropolitan University (Grant ID: Cardiff Metropolian (Internal))
Yn dangos eitemau sy’n perthyn drwy deitl, awdur, pwnc a chrynodeb.
Thomas, Andrew J.; Byard, Paul; Francis, Mark; Fisher, Ron; White, Gareth R.T. (Emerald Group Publishing Limited, 2015)Purpose – The purpose of this paper is to identify the tools, methods and models that UK manufacturing companies adopt and apply in order to achieve resiliency and economic sustainability. The results of this work can ...
'In vitro' tensile tests and corrosion analyses of a rapid manufacture-produced cobalt-chromium alloy compared to cast cobalt-chromium alloys Alifui-Segbaya, Frank (Cardiff Metropolitan University, 2011)In this age of technological advancement in dentistry, the traditional method of manufacturing removable partial denture frameworks could be supplemented with rapid manufactured (RM) denture frameworks when the technology ...
Resilience and vulnerability: Supporting the integration of unaccompanied asylum-seeking minors in the United Kingdom Wells, Mike (Cardiff Metropolitan University, 2017)There is a general agreement in the existing research that unaccompanied asylum-seeking minors (UAMs) are a particularly vulnerable group as a result of their traumatic experiences of forced migration and displacement ...